JIS Snc815 Steel Bar 12crni3 Alloy Steel Round Bar
Deskripsyon Product
1. Konpozisyon chimik
| C | Si | Mn | P | S | Kr | Ni |
| 0.10-0.17 pousan | 0.17-0.37 pousan | 0.30-0.60 pousan | Mwens pase oswa egal a 0.035 pousan | Mwens pase oswa egal a 0.035 pousan | 0.60-0.90 pousan | 2.75-3.15 pousan |
2. Ekivalan Steel Klas
| ASTM A29 | JIS G4105 | GB | DIN | EN | TOCT |
| 3415 | SNC815 | 20CrNi3 | 1.5752 | 15CrNi13 | 12XH3A |
3.Mechanical Pwopriyete
Tensile Fòs (MPA) | Sede fòs (MPA) | Rediksyon (pousan) | Elongasyon (10 pousan) | Fòs enpak (Aku2/J) | Dite (HB) |
| 930 | 735 | 11 | 50 | 71 | 217 |
4. Tretman andigman
Plak: Orijin Nwa, Orign frèt woule klere, usinage, Grinded
Bar: Orijin Nwa, Orign woule frèt (trase) klere, vire, kale, moulen
5. Tretman chalè
1) Recuit
Chofe a 780-850ºC, fre dousman nan gwo fou. Sa a pral pwodwi yon maksimòm dite Brinell nan 217.
2) soulaje estrès
Soulaje estrès pou retire estrès machin yo ta dwe te pote soti nan chofaj a 650 ° C, kenbe pou yon èdtan nan chalè, ki te swiv pa lè refwadisman. Operasyon sa a fèt pou diminye deformation pandan tretman chalè.
3) Redi
Redi soti nan yon tanperati 830-870ºC ki te swiv pa lwil oliv trempe. Dite apre trempe se 64 HRC.
4) tanperaman
Tanperati tanperaman: 180-200ºC.
5) Forge
Tanperati cho fòme: 1200-1800ºC.
6) soude
Sa a se yon alyaj kabòn segondè tipikman yo itilize nan aplikasyon pou pote kote soude pa aplikab oswa apwopriye.