Deskripsyon Product
NM400 NM500 usure rezistan plak asye mete plak
Plak ki reziste abrasion AR400 AR500
Asye ki reziste abrazif
Plak asye difisil
difisil 500 difisil 400
plak asye koupe ak koube
1.Pwosesis Pwodiksyon
1)SteelmakPwosesis Flow Chart
Blast Furance plis cho an metal louch kamyon plisKRTretman metal cho plis konvètisè plis LF raffinage founo plis RH vakyòm degaze furance plis kon-cast
2.Rolling Pwosesis Flow Chart
Rechofaj Furance plis Dekalifikasyon dlo a wo-presyon plis Moulen Edger plis Moulen degrosaj plis Moulen fini plis refwadisman akselere plis nivelman cho plis Marking ak enprime espre plis Kabann refwadisman plis UT sou liy plis taye rekòt plis taye taye doub-bò plis koupe-a- longè Chea plis Mezi plis Marking ak Flite Enpresyon plis Fwad Leveler/Chalè tretman
3.Chalè-Tretman Flow Chart
Plak plis piki eksplozif plis Trempe Furance plis Trempe Machine plis Tanperaman Furance plis Warm Leveler plis Refroidissement Kabann plis Koupe plis Cold Leveler plis Fini & Emballage
4.Thickness ak Lajè
Epesè: 4.5mm-150mm
Lajè: 1600mm-4100mm
5.Main Klas
Almay: XAR400, XAR450, XAR500, XAR600, Dillidur400, Dillidur500
Bèljik:QUARD400,QUARD450,QUARD500
Frans: FORA400, FORA500, Creusabro4800, Creusabro8000
Baosteel: B-HARD360, B-HARD400, B-HARD450, B-HARD500
HBIS:NM360,NM400,NM450,NM500
Fenlann: RAEX400,RAEX450,RAEX500
Japon: JFE-EH360, JFE-EH400, JFE-EH500, WEL-HARD400, WEL-HARD500
6.Chemical Konpozisyon & Pwopriyete
| Klas | c | Si | Mn | P | S | Al | Cr plis Ni plis Mo | Nb plis V plis Ti |
| NM400 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Max 0.9 | Trace Kantite lajan |
| NM450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Maksimòm 1.2 | |
| NM500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Maksimòm 1.5 | |
| NM550 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Max 2.0 | |
| NM600 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Maksimòm 2.5 | |
| XCHD400 | 0.10-0.30 | 0.20-0.40 | 1.00-2.00 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Max 0.1 | |
| XCHD450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Max 0.9 | |
| XCHD500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | Maksimòm 0.015 | Maksimòm 0.003 | Min 0.020 | Maksimòm 1.5 |
7.
| Klas | Gwosè (mm) | RP0.2(Mpa) | Rm (Mpa) | A50(pousan) | AKV,(ºC) | KV2(J) | HBW | ||
| NM400 | 100 | 1233 | 1337 | 15 | -20 | 35 | 37 | 42 | 415 |
| NM450 | 60 | 1345 | 1434 | 9.5 | -20 | 72 | 59 | 58 | 455 |
| NM500 | 50 | 1608 | 1706 | 10.5 | -20 | 43 | 50 | 45 | 495 |
| XCHD400 | 35 | 1025 | 1161 | 17.5 | -40 | 52 | 45 | 40 | 413 |
| XCHD450 | 30 | 1281 | 1400 | 10.5 | -40 | 45 | 48 | 52 | 453 |
| XCH500 | 6 | 1465 | 1529 | 13.5 | -40 | 24 | 24 | 22 | 515 |
Ekspozisyon pwodwi
1) Teknik Faktori
Koupe gwo plak asye kòm kondisyon ou yo fè sifas la nan plak la klere pa miling ak fanm k'ap pile, tou ka fè twou ak fè degre ang, epi yo ka soude pa desen ou an.
Pou epesè anba 30mm, koupe pa lazè; Pou epesè plis pase 30mm, sitou OXY-koupe, koupe flanm dife.
Pou plak asye 200mm epesè a, paske pandan koupe flanm dife a, tanperati a wo anpil, kidonk plak asye koupe pati yo ka kase nan pati ang lan, Lè sa a, travayè nou yo pral repare ang yo pou yo bon kondisyon.
2) Aplikasyon
Mete ki reziste plak asye ak rezistans segondè mete ak bon pèfòmans enpak se yon bon bagay, ka koupe, koube, soude, elatriye, ka adopte soude, ploge soude, koneksyon boulon fason konekte ak lòt estrikti, tankou sèn nan antretyen an. pwosesis posede karakteristik sa yo nan ekonomize tan, pratik ak lajman ki itilize nan metaliji, chabon, siman, estasyon elektrik, vè, min, materyèl bilding, brik ak endistri pétrochimique, konpare ak lòt materyèl, gen yon pèfòmans pri segondè, li te favorize pa plis. ak plis achtè.
Baj popilè: nm500 usure rezistan plak asye ar500, Lachin, manifaktirè, Swèd, faktori