T4 gwo vitès asye zouti (T4, 1.3255, S 18-1-2-5, SKH3)
T4 Asye Wonn Bar: dyamèt 2mm - 200mm
T4 Asye Flat: epesè 2-20mm x lajè 10-100mm
T4 Plak Asye: epesè 2-200mm x lajè 200-810mm
Sifas Fini: Nwa, Rough machin, vire oswa kòm pou chak kondisyon yo bay.
2.Ki enpòtan espesifikasyon asye nan Ezi T4 gwo vitès Asye zouti
Peyi | ETAZINI | Alman | Japon |
Standard | ASTM A600 | DIN EN ISO 4957 | JIS G4403 |
Nòt | T4/T12004 | S 18-1-2-5 / 1.3255 | skh3 |
3.AISI T4 Asye Zouti ak konpozisyon chimik ekivalan '
ASTM A600 | C | Mn | P | S | sizo | Cr | V | W | Mouvman | Kolòn | ||||||||
T4 | 0.70 | 0.80 | 0.10 | 0.40 | 0.03 | 0.03 | 0.20 | 0.40 | 3.75 | 4.50 | 0.80 | 1.20 | 17.50 | 19.00 | 0.40 | 1.00 | 4.25 | 5.75 |
DIN ISO 4957 | C | Mn | P | S | sizo | Cr | V | W | Mouvman | Kolòn | ||||||||
S 18-1-2-5 / 1.3255 | 0.75 | 0.83 | ... | 0.40 | 0.03 | 0.03 | ... | 0.45 | 3.80 | 4.50 | 0.80 | 1.20 | 17.50 | 18.50 | 0.50 | 0.80 | 4.50 | 5.50 |
JIS G4403 | C | Mn | P | S | sizo | Cr | V | W | Mouvman | Kolòn | ||||||||
skh3 | 0.73 | 0.83 | ... | 0.40 | 0.03 | 0.03 | ... | 0.45 | 3.80 | 4.50 | 0.80 | 1.20 | 17.00 | 19.00 | ... | ... | 4.50 | 5.50 |
4.Segondè vitès asye T4 Zouti Asye pwopriyete mekanik
Pwopriyete fizik nan gwo vitès T4 Asye zouti
Pwopriyete fizik (valè mwayèn) nan tanperati anbyen
Modil elastisite [103 x N/mm2]: 217
Dansite [g/cm3]: 8.70
Kondiktivite tèmik [W/M.K]: 19.0
Rezistans elektrik [Ohm mm2/m]: 0.65
Espesifik kapasite chalè [J/g.K]: 0.46
Pwopriyete mekanik T-4 Asye
Pwopriyete yo | Metrik | Imperial |
Modil elastisite | 190-210 GPa | 27557-30458 ksi |
Pousantaj pwazon | 0.27-0.30 | 0.27-0.30 |
Pwopriyete tèmik nan T4 Asye Zouti
Pwopriyete yo | Metrik | Imperial |
Ekspansyon tèmik ko-efisyan | 11.9 μm/m°C | 6.6 μin/in°F |
5.Forging nan ASTM T4 Zouti Asye Materyèl Asye
Fòje nan T4 asye ka te pote soti nan 850 a 1120 ° C (1775 a 2100 ° F).
Chofe T4 asye materyèl inifòm ak tou dousman nan 860-880 ° C.
Ogmante tanperati a fòje jiska 1050-1120 ° C.
T4 hss asye zouti yo ta dwe refwadi trè dousman apre fòje.
6.AISI / ASTM T4 Zouti Asye Tretman chalè ak pwopriyete yo
redisman
Harden T4 gwo vitès asye soti nan yon tanperati nan 1260-1290oC ki te swiv pa lwil oliv, lè a oswa beny cho nan 550oC. Dite apre yo fin depanse se 63-66 HRC.
Annealing
T4 asye yo ta dwe anne apre travay cho. Ogmante tanperati a nan T4 gwo vitès asye a 860 ° C (Max220 ° C pou chak èdtan). Kenbe nan tanperati a ak Lè sa a, fre tou dousman ak founo dife a. Dite annealed reyalize yo ta dwe anba a HB255.
Aristid
Tanperati tanperati: 2x 560-580oC. Dite apre aprè apeze se 64-65 HRC.
7.Aplikasyon pou ASTM / AISI T4 Asye
Ezi T4 gwo vitès asye zouti yo lajman itilize kòm zouti koupe, broach ak ponch frèt, vire, planifye ak kouto fraisaj pou travay ki graj.
Aplikasyon tipik yo se:
Egzèsis,
Milling Kouto,
Fil koupe Zouti,
Knurling Zouti,
Fwad ekstrizyon ponch
Broaches elatriye