1.2080 asye, souvan ke yo rekonèt kòm ASTM D3, se yon wo-kabòn wo-chromium frèt zouti asye ak yon konpozisyon chimik nan 2.1% kabòn ak plis pase 11% CHROMIUM, ki se yon alyaj trè dirab ak korozyon ki reziste. Asye sa a defini dapre DIN 17350, ki bay lis espesifikasyon pou divès kalite asye zouti. 1.2080 asye gen dite ekselan, rezistans mete, severite ak retansyon kwen ekselan ak estabilite dimansyon, epi li se lajman ki itilize nan envantè de zouti, mwazi, près ak lòt aplikasyon ki sanble.

Production equipment

Eleman chimik:

KANPE	C(%)	Mn(%)	P(%)	S(%)	Si (%)	Cr (%)	V(%)	W(%)
ASTM A681-08	2.00-2.35	0.10-0.60	Mwens pase oswa egal a 0.030	Mwens pase oswa egal a 0.030	0.10-0.60	11.00-13.50	Mwens pase oswa egal a 1.00	Mwens pase oswa egal a 1.00
JIS G4404: 2006	1.40-1.60	Mwens pase oswa egal a 0.60	Mwens pase oswa egal a 0.030	Mwens pase oswa egal a 0.030	0.40	11.00-13.00	0.20-0.50	-
EN ISO 4957:1999	1.90-2.20	0.20-0.60	-	-	0.10-0.60	11.00-13.00	-	-
ISO 4957: 1999	1.90-2.20	0.20-0.60	-	-	0.10-0.60	11.00-13.00	-	-

2.DIN 1.2080/X210Cr12 STEEL KI GENYEN ESTANDA & EKIVILAN KLAS

ETAZINI	Japonè	Jeman	Britanik	Lafrans	tretman chalè	Chinwa
ASTM&AISI&SAE	ANNWI	EN DIN	ENI BS	EN NF	ISO	GB
AISI D3	SKD1	X210Cr12			K100	Cr12

3.DIN 1.2080 asye Recuit

Tanperati a annealing jeneral nan asye DIN 1.2080 se 850-870 degre, ak tan an kenbe se 3-6 èdtan, ak Lè sa a, fou a refwadi a 500-600 degre ak pousantaj la 30 degre / h max.Annealed dite anjeneral anba a 248HBW.